基本性质/ TYPICAL CHARACTERISTICS
型式/ Type : 弱酸型阳离子交换树脂/Weak acid cation exchange resin
结构/ Matrix structure : 巨孔状交叉键结聚苯乙烯/
Macroporous cross1inked polystyrene
官能基/ Functional group : Iminodiacetic
物理型式/ Physical form : 含水球状/ Moist spherical beads
离子型式/ Ionic as shipped : 钠/ Sodium
粒径分布/ Screen size USS(wet) : 16 to 50
粒径大小/ Particle size : 0.3 to 1.2 mm
总交换容量/Total Exc. Capacity : 1.8 meq/ml (H+)
膨胀系数/ Swelling (approx.) : H+ → Na+ 20%
含水份/ Moisture : 45-50%
pH 作范围/ Suitable pH range : 0 to 14
溶解率/Solubility : 不溶解于任何溶剂/ Insoluble in 免费信息mon solvents
逆洗沉降密度/Backwash settled density : 0.72 to 0.79 g/ml

建议操作条件/ OPERATING CONDITIONS
操作温度/ Max .Operating Temperature : 70oC
流速/ Service flow : 10 – 30 BV/hr
逆洗膨胀空间/Backwash expansio ace : 50 to 70%
逆洗流速/ Backwash expansion flow : 8-10 BV/hr
再生/ Regeneration
酸浓度/ Concentration of acid : 5 - 8%
流速/ Flow rate : 3 – 4 BV/hr
再生酸药剂量/ Regeneration quantity: 150-200 g/lit of HCl
:200-250g/lit of H2SO4
慢洗流速/ Rinse flow rate : 3 – 4 BV/hr
若需要转成Na离子/ Conversion to sodium form if required
浓度/ Concentration : 2-4%
流速/ Flow : 4 BV/hr
盐药量/ NaOH quantity : 50-150 g/lit
慢洗流速/ Rinse flow rate : 3 – 4 BV/hr

应用附注/ APPLICATION NOTE
金属离子的选择性是依据进流液的pH 而决定在某些的pH 范围内, 交换容量会很严重的下降.
最有效的除铜pH : 3 - 4
Effective pH for copper removal
最有效的除镍pH : 3 - 5
Effective pH for nickel removal
最有效的除铁pH : 2 - 4
Effective pH for iron removal
最有效的除铅pH : 2 以上
Effective pH for lead removal
最有效的除锰pH : 4 以上
Effective pH for manganese
选择性的顺序如下:
Order of selectivity is as follows
Cu > Pb > Ni > Zn > Co > Cd > Fe+3 > Mn > Mg > Ca >> Na
再生药剂的选择可用盐酸或硫。对于除铜应用, 建议用硫酸! 建议用硷NaOH 再生将树脂转换成Na 型, 并将pH 变成原来的进水条件。